Okayama Giken (Mining) Co., Ltd. Erbjuder kinesisk hög renhet magnesia aluminiumoxid spinel med utmärkt motstånd mot termisk chock och slaggattack. Denna spinel finns i flera storlekar och är idealisk för stålhalor, tundor och högpresterande castables.
Magnesia-Alumina Spinel (MAS) in China is a synthetic refractory material formed by combining magnesium oxide (MgO) and aluminum oxide (Al₂O₃) under high temperatures. It is known for its excellent thermal stability, corrosion resistance, and structural integrity at extreme temperatures, making it ideal for demanding industrial applications.
Spinel is typically produced through one of two methods:
Sintered Spinel – made by calcining a blend of magnesia and alumina at temperatures above 1700°C.
Fused Spinel – created by melting MgO and Al₂O₃ in an electric arc furnace, then cooling and crushing the material into desired sizes.
Both types are widely used, with sintered spinel offering cost-efficiency and fused spinel providing higher purity and density.
Magnesia-Alumina Spinel is widely used in:
Refractory castables and Mas bricks for steelmaking (ladles, tundishes, electric arc furnaces)
Cement rotary kilns
Foundry and non-ferrous metal industries
High-performance insulating linings
Anti-corrosion coatings and repair materials
Its resistance to slag attack, thermal shock, and alkali corrosion makes it a preferred material in high-temperature industrial environments.
Spinel is available in aggregates (0–1mm, 1–3mm, 3–5mm, 5–8mm) and fine powders (100 mesh, 200 mesh, 325 mesh), suitable for both shaped and monolithic refractory applications.
| Brand | AL2O3 | MgO | FE2O3 | SiO2 | CaO | B.D. |
| M70 | ≥74% | 22-24% | ＜0.25% | ＜0.15% | ＜0.30% | ＞3.3g/cm³ |
| M90 | 88-91% | 8-10% | 8-10% | ＜0.30% | ＜0.30% | ＞3.3g/cm³ |